(en)This invention relates to latex compositions that incorporate at least one bioactive component such as an antibacterial or an antifungal agent, and methods for making and using such latex compositions. The latex compositions disclosed herein can be prepared by the emulsion polymerization of the latex component monomers in the presence of the at least one bioactive component.

1.ApplicationNumber: US-89553907-A
1.PublishNumber: US-8785519-B2
2.Date Publish: 20140722
3.Inventor: KRISHNAN VENKATARAM

4.Inventor Harmonized: KRISHNAN VENKATARAM(US)

5.Country: US
6.Claims:
(en)This invention relates to latex compositions that incorporate at least one bioactive component such as an antibacterial or an antifungal agent, and methods for making and using such latex compositions. The latex compositions disclosed herein can be prepared by the emulsion polymerization of the latex component monomers in the presence of the at least one bioactive component.

7.Description:
(en)REFERENCE TO RELATED APPLICATION
This application claims priority to U.S. Ser. No. 60/839,892, filed on Aug. 24, 2006, the contents of which are hereby incorporated by reference.


TECHNICAL FIELD OF THE INVENTION
This invention relates to the field of polymeric materials that can be used in combination with a wide variety of substrates, such as textiles, metal, cellulosic materials, plastics, and the like, and to the field of bioactive/antimicrobial agents such as antibacterial and antifungal materials.
BACKGROUND OF THE INVENTION
The deposition of latex polymer coatings on solid substrates has long been utilized to impart certain end-use performance properties to those substrates, such as hydrophobicity, strength, adhesive properties, compatibility, and the like. Depending upon the selection of the starting monomers, surfactants, emulsion polymerization conditions, and other parameters, the deposited polymers can be designed to carry an anionic, a cationic, or an amphoteric charge, a feature which directly influences coating performance. Further, the resulting latex polymer can be blended with a range of other functional materials to impart additional or enhanced features to the final coating material.
In a number of applications, latex polymers can be blended with compositions containing bioactive compounds that exhibit antimicrobial activity, in order to provide a latex formulation that can be used in harsh environments where antimicrobial properties are particularly needed. These antimicrobial components are usually employed in relatively small amounts as formulating ingredients that are added after the polymer has been made. While such blends are useful, many practical issues remain in attempts to enhance or control the extent of antimicrobial protection these compositions might afford. For example, such compositions and methods are often inadequate for providing long-term protection of substrates or materials in which they are deployed, especially in their antifungal properties. Methods to augment or to more finely control the antimicrobial properties are also needed. Regulatory issues associated with introducing a new antimicrobial material, namely the polymer, may be significant. Moreover, approaches to prolong or extend the effectiveness of the antimicrobial properties remain elusive.
Therefore, what are needed are new methods and approaches to impart and to enhance antimicrobial activity of latex polymers, as well as the coatings and articles prepared therefrom. What are also needed are methods to more closely manage the antimicrobial activity of such materials, including approaches to extend the effectiveness of their bioactivity.
SUMMARY OF THE INVENTION
This invention encompasses new methods and approaches to incorporate bioactive or antimicrobial ingredients such as antibacterial and antifungal agents into a latex, such that the antimicrobial properties of the latex can be enhanced and controlled. The present invention also relates to new types of bioactive anionic polymer latex materials. In one aspect, this disclosure provides a method for incorporating antimicrobial ingredients into a latex during the emulsion polymerization process. Previously, antimicrobial agents have been added to a latex after the polymerization process and in relatively small amounts as preservatives for the latex product or for the end use application such as paints. The present invention allows the use of higher concentrations of a wide range of bioactive ingredients, including highly hydrophobic bioactive ingredients, which can be readily incorporated into the latices such that the resulting latex particles function as carriers for the active ingredients. The thorough incorporation of an active ingredient in this manner can afford a substantially homogeneous distribution of the additive and result in superior and sustained performance compared to pre-made dispersions.
In one aspect of this invention, the emulsion polymerization is carried out such that the bioactive agents are incorporated into the polymer during the polymerization, typically by dissolving the bioactive component in a monomer stream. In this manner, the bioactive agents can be at least partially encapsulated within the latex polymer matrix. One advantage provided by this process is the ability to incorporate or encapsulate large amounts of bioactive ingredients, including hydrophobic components, without substantially degrading the bioactive agent. In another aspect, this invention also provides a tunable antimicrobial system based on an anionic latex which function as a type of carrier for at least one bioactive ingredient, and optionally further including another bioactive additive that can be blended with the latices disclosed herein. Thus, these latices can have a multifunctional purpose such as providing binding, strength, and dispersion properties in addition to being a carrier for an active functional ingredient, and optionally constituting one component of a blended antimicrobial composition.
In one aspect, because the bioactive ingredients are typically incorporated into a latex during the emulsion polymerization process, these bioactive components can be at least partially encapsulated within the latex polymer matrix. In another aspect, the bioactive components can be substantially encapsulated within the latex polymer matrix. While not intending to be bound by theory, it is believed that, by delivering the active ingredient to a desired end use application, the latex polymer with the encapsulated bioactive ingredients can provide sustained and controlled exposure of the bioactive ingredients to the environment in which they are deployed, thereby providing longer and more effective protection to the product or the application. Moreover, because the bioactive anionic latices can be formed by existing emulsion polymerization processes, the polymerization methods advantageously allow for the preparation of high molecular weight polymers.
In a further aspect, the methods disclosed herein also provide the potential to adjust the antimicrobial behavior using a combination of approaches to deploy the antimicrobial agent. For example, highly tailored antimicrobial properties can be imparted to a product by both incorporating the bioactive ingredient into a latex during the emulsion polymerization process, and by combining the resulting latex product with the same or at least one different bioactive component in a blend. This approach allows antimicrobial properties to be selected and adjusted using the polymer, the additive, or both, depending on the circumstances and the performance required.
In yet a further aspect, the techniques disclosed herein can provide the ability to encapsulate larger amounts of the active ingredient into a latex composition than are afforded by standard methods. For example, antimicrobial components are usually employed in relatively small amounts as formulating ingredients once the latex polymer has been prepared, and such bioactives typically are utilized at concentrations ranging up to about 1000-2000 ppm. In contrast, the antimicrobial component of the latex compositions of this invention can be utilized in concentrations as high as about 40 weight percent based on the total monomer weight. In this aspect, this invention can provide stable, concentrated dispersions that can be used as such, or as an additive, or concentrated dispersions that can be diluted and added to other systems which require antimicrobial protection. High antimicrobial component concentrations provide flexibility and ensure the utility of these latex compositions as concentrates as well as in non-concentrated form.
While the methods disclosed herein can be applied to any bioactive agent that a particular end use requires, the present disclosure is primarily drawn to providing or enhancing the antimicrobial properties of a latex, substrate, or particular end product. The relevant antimicrobial activity can include antibacterial activity, antifungal activity, antiviral activity, antiparasitic activity, or any combination thereof, depending upon the particular selection of bioactive agents. As used herein, the general term “bioactive” component, agent, or ingredient is used interchangeably with the term “antimicrobial” component, agent, or ingredient.
In another aspect, this invention provides a bioactive anionic polymer latex comprising:
a) a latex polymer comprising the polymerization product of: i) at least one ethylenically unsaturated first monomer; and ii) optionally, at least one ethylenically unsaturated second monomer that is anionic or a precursor to an anion; b) at least one bioactive component at least partially encapsulated within the latex polymer; and c) optionally, at least one sterically bulky component incorporated into the latex polymer.

While the inventive latices of this disclosure are anionic in nature, it is not necessary that the anionic charge of these latices be imparted by a monomer that is anionic or a precursor to an anion, that is, an anionic monomer. For example, an anionic initiator or an anionic surfactant that can be polymerizable or non-polymerizable can be used to introduce the anionic charge to the inventive latices. Accordingly, in this aspect, the at least one ethylenically unsaturated second monomer that is anionic or a precursor to an anion is described as an optional feature of the bioactive anionic polymer latex.


When more than one ethylenically unsaturated first monomer is used to constitute the first monomer component, each of these first monomers is selected independently. Similarly, when more than one ethylenically unsaturated second monomer that is anionic or a precursor to a anion, referred to herein as the “anionic” monomer, is used to constitute the second monomer component, each of these second monomers is selected independently. A wide range of weight percentages of the at least one first monomer and the at least one second monomer can be used in this invention. For example, the latex can comprise from about 0.01 percent to 100 percent by weight of the ethylenically unsaturated first monomer, based on the total monomer weight, and the latex can comprise from 0 percent to about 99.99 percent by weight of the ethylenically unsaturated second monomer that is anionic or a precursor to an anion, based on the total monomer weight.
Further, the latices of this invention can also comprise a sterically bulky component which is incorporated into the anionic polymer latex to sterically stabilize the latex. These sterically bulky components can include, but are not limited to, monomers, polymers, and mixtures thereof as set forth below. Thus, a monomer can be incorporated as a co-monomer that can attach to, or constitute a portion of, the backbone of the anionic polymer, examples of which include an alkoxylated ethylenically unsaturated third monomer. A polymer can be incorporated by adsorbing or being grafted onto the latex surface, an example of which includes polyvinyl alcohol.
While the at least one sterically bulky component incorporated into the latex polymer is an optional component, this invention also provides for use of a wide range of amounts and concentrations of this component. Thus, as will be understood by the skilled artisan, in bioactive anionic polymer latices that do not incorporate at least one sterically bulky component, latex stability can be enhanced by increasing the relative proportion of the anionic second monomer, by varying the amount and type of the initiator used, by the addition of surfactants such as nonionic or anionic surfactants, and the like, or any combination of such methods. The relative proportion of the anionic second monomer can be reduced and/or surfactants can be eliminated in the presence of at least one sterically bulky component.
In still another aspect, this invention provides a method of making a bioactive anionic polymer latex comprising initiating an emulsion polymerization of an aqueous composition comprising, at any time during the emulsion polymerization:
a) at least one ethylenically unsaturated first monomer; b) optionally, at least one ethylenically unsaturated second monomer that is anionic or a precursor to an anion; c) at least one anionic surfactant; d) at least one bioactive component; e) at least one free-radical initiator; f) optionally, at least one sterically bulky ethylenically unsaturated third monomer; g) optionally, at least one sterically bulky polymer; and h) optionally, at least one nonionic surfactant.

In this aspect, because the anionic latices of this invention carry a net negative charge, when an anionic latex is prepared in the absence of the optional second anionic monomer, the overall negative charge of the latex can be imparted to the latex by a free radical initiator, by an anionic surfactant, by an anionic sterically bulky component, or by any combination thereof.


In one aspect of the invention, the at least one bioactive component can be dissolved in the monomer feed at any time during the emulsion polymerization process. Further, in another aspect, the aqueous composition components and the at least one bioactive component can be provided as a dispersion prior to initiating the emulsion polymerization. Thus, this invention provides for batch processes, in which the at least one bioactive component is present in the seed stage. In this aspect, the emulsion polymerization is initiated when all the components of the composition, including the at least one bioactive component, are present from the time of initiation. Further, this invention also provides for semi-continuous processes in which the emulsion polymerization is initiated at a time when all components of the composition are not present from the time of initiation, but some are added at various times after initiating the polymerization. In this aspect, for example, the at least one bioactive component can be added at any time after the seed stage. In another aspect, for example, any other component or combination of components provided above can be added at any time after the seed stage, except for at least a portion of the total amount of any component that is required to initiate and propagate an emulsion polymerization. Thus, the bioactive anionic latex provided herein can be made by any variety of batch or by a semi-continuous processes.
In one aspect, the bioactive latices of this invention can be provided or used as coatings, which can be applicable to medical implants, including artificial ball and socket joints, rods, stents, dental implants, pins, screws, catheters, and the like. Such coatings can also be provided on everyday surfaces, such as air-conditioning coils, air filters, pipes, roofing, bathroom items, kitchen items, and the like. Such a coating can prevent microbial infections, such as bacteria and mold, in vehicles as well as homes, hospitals, and other buildings. Further examples of uses of the resultant products are use as an aqueous dispersion or directly in powder form, for example, for sterilizing cooling-water circuits, or indirect use, for example by addition to paints or other surface coatings.
These and other features, aspects, embodiments, and advantages of the present invention will become apparent after a review of the following detailed description of the invention. It should be understood, however, that these aspects, embodiments, and examples are provided for illustrative purposes only, and are not to be construed in any way as imposing limitations upon the scope thereof.


DETAILED DESCRIPTION OF THE INVENTION
The present invention provides new latex polymeric materials that can be used in combination with a wide variety of substrates, such as textiles, metal, cellulosic materials, plastics, and the like, in which the polymeric materials include bioactive components incorporated into the latex polymer. This invention also provides new methods and processes that allow incorporating high concentrations of an active ingredient such as antifungal agents during the emulsion polymerization. In one aspect, for example, the disclosed process can be used to incorporate from about 0.01% to about 40%, based on the total monomer weight (“phm” or parts per hundred of monomer), of a substantially hydrophobic bioactive ingredient during the emulsion polymerization. While the bioactive ingredient can be introduced at any stage during the polymerization process including very early during the seed formation stage, in one aspect, the bioactive component or additive (bioadditive) can be added during the later stages of polymerization process, for example, when from about 30% to about 90% of the monomer has been fed into the polymerization reactor.
Useful bioactive additives can be solids, liquids, or combinations thereof. Many of the bioactive additives that can be employed in this invention are substantially water insoluble or have limited solubility in water. In this aspect, the typical water insoluble, hydrophobic bioactive agent can be soluble in at least one of the monomers employed in the emulsion polymerization. Thus, the typical hydrophobic bioactive ingredient can be introduced into the polymerization reactor by substantially or partially dissolving it in a monomer feed at the appropriate time. Therefore, the typical ingredients chosen for imparting antimicrobial properties usually will be soluble in the monomers that are used to make the polymer latex. In another aspect, useful bioactive additives in this invention can also be substantially water soluble, examples of which include o-phenylphenate (deprotonated o-phenylphenol), and similar agents. In this aspect, it is not necessary that such a hydrophilic bioactive additive be soluble in any monomer that is to be polymerized.
In another aspect, it is not required that antimicrobial ingredients be soluble in at least one of the monomers used, as these ingredients can also be added as a pre-made dispersion in water. In this aspect, the dispersions can be made, among other ways, by using a relatively concentrated amount of the additive and dispersing by using surfactants, dispersants, and the like, and typically employing a mixing device such as a high speed mixer, a homogenizer, an Eppenbach mixer, or similar devices. In such a case, the dispersion can be fed into the reactor to deliver the appropriate amount of active ingredient into the latex.
In one aspect, this invention encompasses a bioactive anionic polymer latex comprising:
a) a latex polymer comprising the polymerization product of: i) at least one ethylenically unsaturated first monomer; ii) optionally, at least one ethylenically unsaturated second monomer that is anionic or a precursor to an anion; b) at least one bioactive component at least partially encapsulated within the latex polymer; and c) optionally, at least one sterically bulky component incorporated into the latex polymer.

As provided herein, the at least one sterically bulky component incorporated into the latex polymer can be selected independently from at least one sterically bulky ethylenically unsaturated third monomer, at least one sterically bulky polymer, or any combination thereof. Each of these components, as well as optional or additional components, is considered herein.


In another aspect, this invention also encompasses a method of making a bioactive anionic polymer latex comprising initiating an emulsion polymerization of an aqueous composition comprising, at any time during the emulsion polymerization:
a) at least one ethylenically unsaturated first monomer; b) optionally, at least one ethylenically unsaturated second monomer that is anionic or a precursor to an anion; c) at least one anionic surfactant; d) at least one bioactive component; e) at least one free-radical initiator; f) optionally, at least one sterically bulky ethylenically unsaturated third monomer; g) optionally, at least one sterically bulky polymer; and h) optionally, at least one nonionic surfactant.

In yet another aspect, this invention provides a method of making a bioactive anionic polymer latex comprising:
a) providing an aqueous composition comprising:
i) at least one ethylenically unsaturated first monomer; ii) optionally, at least one ethylenically unsaturated second monomer that is anionic or a precursor to an anion; iii) at least one anionic surfactant; iv) optionally, at least one sterically bulky ethylenically unsaturated third monomer; v) at least one free-radical initiator; and vi) optionally, at least one nonionic surfactant;
b) initiating an emulsion polymerization of the composition; and c) adding at least one bioactive component to the composition during the emulsion polymerization process.

In this aspect, at least one anionic surfactant is typically used to prepare the bioactive anionic polymer latex. The at least one anionic surfactant that is employed can be in the form of an anionic surfactant that also does not constitute an ethylenically unsaturated second monomer, or the at least one anionic surfactant can be an ethylenically unsaturated second monomer that is anionic or a precursor to an anion. In the latter case, the second monomer that is anionic or a precursor to an anion functions both as an ethylenically unsaturated second monomer and as an anionic surfactant. In any event, when an anionic latex is prepared in the absence of the optional second anionic monomer, the overall negative charge of the latex can be imparted to the latex by a free radical initiator, by an anionic surfactant, by an anionic sterically bulky component, or by any combination thereof.
Many compounds and species that can be used as ethylenically unsaturated first monomers and sterically bulky components are disclosed in the European Patent Number EP 1109845 and the corresponding PCT Published Patent Application WO 00/8008077, each disclosure of which is incorporated herein by reference in its entirety.
Ethylenically Unsaturated First Monomers
Various ethylenically unsaturated first monomers can be used in the latex of the present invention. Examples of suitable first monomers can be found at least in U.S. Pat. No. 5,830,934, U.S. Patent Application Publication Numbers 2005/0065284 and 2005/0003163, and European Patent Number EP 1109845, all to Krishnan, each disclosure of which is incorporated herein by reference in its entirety. In this aspect, examples of such monomers include, but are not limited to, vinyl aromatic monomers, halogenated or non-halogenated olefin monomers, aliphatic conjugated diene monomers, non-aromatic unsaturated mono- or dicarboxylic ester monomers, unsaturated alkoxylated monoester or diester monomers, unsaturated diesters of an acid anhydride monomer, nitrogen-containing monomers, nitrile-containing monomers, cyclic or acyclic amine-containing monomers, branched or unbranched alkyl vinyl ester monomers, aryl vinyl ester monomers, halogenated or non-halogenated alkyl(meth)acrylate monomers, halogenated or non-halogenated aryl(meth)acrylate monomers, carboxylic acid vinyl esters, acetic acid alkenyl esters, carboxylic acid alkenyl esters, a vinyl halide, a vinylidene halide, or any combination thereof, any of which having up to 20 carbon atoms. Thus, the ethylenically unsaturated first monomer is selected from a monomer that is not anionic and is not a precursor to an anion under the reaction and workup procedures. It is the Applicant's intent to disclose both acrylate and methacrylate moieties when either moiety is disclosed in a suitable monomer. Thus, the disclosure that an acrylate monomer is a suitable ethylenically unsaturated first monomer also encompasses the disclosure that the corresponding methacrylate monomer is also a suitable first monomer. The abbreviation (meth)acrylate can be used to represent such a disclosure.
Many different ethylenically unsaturated first monomers can be used in preparing the bioactive latices of this invention. In one aspect, suitable examples of ethylenically unsaturated first monomers include, but are not limited to, styrene, para-methyl styrene, chloromethyl styrene, vinyl toluene, ethylene, butadiene, methyl(meth)acrylate, ethyl(meth)acrylate, propyl(meth)acrylate, butyl(meth)acrylate, pentyl(meth)acrylate, glycidyl(meth)acrylate, isodecyl(meth)acrylate, lauryl(meth)acrylate, (meth)acrylonitrile, (meth)acrylamide, N-methylol(meth)acrylamide, N-(isobutoxymethyl)(meth)acrylamide, vinyl neodecanoate, vinyl versatate, vinyl acetate, C 3 -C 8 alkyl vinylethers, C 3 -C 8 alkoxy vinyl ethers, vinyl chloride, vinylidene chloride, vinyl fluoride, vinylidene fluoride, trifluoroethylene, tetrafluoroethylene, chlorotrifluoroethylene, hexafluoropropylene, chlorotrifluoroethylene, perfluorobutyl ethylene, perfluorinated C 3 -C 8 alpha-olefins, fluorinated C 3 -C 8 alkyl vinylethers, perfluorinated C 3 -C 8 alkyl vinylethers, perfluorinated C 3 -C 8 alkoxy vinyl ethers, and the like, or any combination thereof. Thus, halogenated analogs of suitable ethylenically unsaturated first monomers are encompassed by this disclosure, and it is Applicant's intent to disclose any and all suitable halogen-substituted analogs or derivatives of these monomers, including fluorine-substituted analogs, chlorine-substituted analogs, bromine-substituted analogs, and iodine-substituted analogs. The term “halogen-substituted” is meant to include partially halogen substituted and perhalogen substituted, in which any halogen substituents can be the same or can be different. In this aspect as well, it is the Applicant's intent to disclose both acrylate and methacrylate moieties when either moiety is disclosed in a suitable monomer.
In another aspect, the ethylenically unsaturated first monomer can be halogenated or can be non-halogenated. Similarly, the ethylenically unsaturated first monomer can be fluorinated or can be non-fluorinated. For example, fluorinated analogs of alkyl acrylates or methacrylates can be used, as well as the non-fluorinated compounds. The ethylenically unsaturated first monomer can also be chlorinated or can be non-chlorinated. The ethylenically unsaturated first monomer can also be brominated or can be non-brominated. The ethylenically unsaturated first monomer can also be iodinated or can be non-iodinated. For example, fluorinated analogs of alkyl acrylates or methacrylates can be used, as well as the non-fluorinated compounds.
In yet another aspect of this invention, the latices provided herein can comprise from about 0.01 percent to 100 percent by weight of the ethylenically unsaturated first monomer, based on the total monomer weight. In this aspect, the latex of this invention can also comprise from about 0.1 percent to about 99.9 percent, from about 1 percent to about 99 percent, from about 5 percent to about 98 percent, from about 10 percent to about 95 percent, from about 25 percent to about 92 percent, from about 35 percent to about 90 percent, from about 50 percent to about 87 percent, or from about 65 percent to about 85 percent by weight of the ethylenically unsaturated first monomer, based on the total monomer weight. In this aspect, the Applicant's intent is to disclose individually each possible number that such ranges could reasonably encompass, as well as any sub-ranges and combinations of sub-ranges encompassed therein. Suitable weight ranges of the at least one ethylenically unsaturated first monomer are a function of the design properties and the intended use of the material, as appreciated by the skilled artisan.
Optional Ethylenically Unsaturated Anionic Second Monomers
In still another aspect, the latex polymer of the present invention also comprises the polymerization product of at least one ethylenically unsaturated second monomer that is anionic or a precursor to an anion. As provided herein, the at least one ethylenically unsaturated second monomer can be collectively referred to by the term “anionic monomer,” that is, any monomer which possesses or can be made to posses a negative charge. In one aspect, this negative charge may be imparted as a result of hydrolysis and formation of an acidic functionality that is readily deprotonated, or by way of another reaction known to one of ordinary skill that can result in a negatively-charged moiety. Such a reaction, for example a hydrolysis reaction, can take place at any stage in the emulsion polymerization process, such as in the component monomer, in an oligomer, in the resulting polymer, or any combination thereof. In another aspect, the negative charge may result from a pre-existing acid or salt functionality in the component monomer used to prepare the latex polymer. The anionic monomer is typically incorporated into the latex polymer by virtue of its ethylenic unsaturation.
Examples of suitable anionic monomers can be found at least in U.S. Patent Application Publication Numbers 2005/0065284 and 2005/0003163, to Krishnan. In this aspect, examples of suitable anionic monomers include, but are not limited to, a monomer based on the half ester of an unsaturated dicarboxylic acid monomer, an unsaturated mono- or dicarboxylic acid monomer, a sulfate-containing monomer, a sulfonate-containing monomer, a phosphate-containing monomer, a phosphonate-containing monomer, an unsaturated anhydride, a monoester of an acid anhydride, or any combination thereof, any of which having up to 20 carbon atoms. When more than one ethylenically unsaturated second monomer is used to constitute the anionic monomer component, each anionic monomer is selected independently.
Further, suitable examples of ethylenically unsaturated anionic monomers that can be used in the latex of the present invention include, but are not limited to, (meth)acrylic acid, maleic acid, maleic anhydride, 2-sulfoethyl(meth)acrylate, styrene sulfonate, 2-acrylamido-2-methylpropane sulfonic acid, monomethyl maleate, itaconic acid, itaconic anhydride, fumaric acid, or any combination thereof.
As described for the first monomers, halogenated analogs of suitable ethylenically unsaturated second monomers are also encompassed by this disclosure, and it is Applicant's intent to disclose any and all suitable halogen-substituted analogs or derivatives of these monomers, including fluorine-substituted analogs, chlorine-substituted analogs, bromine-substituted analogs, and iodine-substituted analogs. The term “halogen-substituted” is meant to include partially halogen substituted and perhalogen substituted, in which any halogen substituents can be the same or can be different. In this aspect as well, it is the Applicant's intent to disclose both acrylate and methacrylate moieties when either moiety is disclosed in a suitable monomer.
In a further aspect, the latex polymer of this invention can comprise from 0 to about 99.99 percent by weight of the ethylenically unsaturated second monomer that is anionic or a precursor to an anion, based on the total monomer weight. In this aspect, the latex of this invention can also comprise from about 0.01 to about 99 percent, from about 0.1 to about 98 percent, from about 0.5 to about 95 percent, from about 1 to about 90 percent, from about 2 to about 80 percent, from about 3 to about 70 percent, from about 4 to about 60 percent, from about 5 to about 50 percent, from about 7 to about 40 percent, from about 10 to about 30 percent, or from about 15 to about 25 percent, by weight of the anionic second monomer, based on the total monomer weight. In this aspect, the Applicant's intent is to disclose individually each possible number that such ranges could reasonably encompass, as well as any sub-ranges and combinations of sub-ranges encompassed therein.
Sterically Bulky Components
As disclosed herein, one aspect of this invention encompasses an anionic polymer latex comprising: a) a latex polymer as disclosed herein; b) at least one bioactive component at least partially encapsulated within the latex polymer; and c) optionally, at least one sterically bulky component incorporated into the latex polymer. The at least one sterically bulky component incorporated into the latex polymer can be selected independently from at least one sterically bulky ethylenically unsaturated third monomer, at least one sterically bulky polymer, or any combination thereof. In this aspect, and while not intending to be bound by theory, this sterically bulky component is typically incorporated into the anionic polymer latex to sterically stabilize the latex.
As used herein, the term “incorporated” with respect to the use of the at least one sterically bulky ethylenically unsaturated third monomer includes, but is not limited to, the attachment of this third monomer to the anionic polymer, for example, by co-polymerization of the third monomer with the first monomer and the optional second monomer disclosed herein, to form the anionic polymer latex. Further, the term “incorporated” with respect to the at least one sterically bulky ethylenically unsaturated third monomer can also include the attachment of this third monomer to the anionic polymer in any other fashion, such as, for example, by grafting onto the polymer backbone. In another aspect, the term “incorporated” with respect to the use of the at least one sterically bulky polymer includes, but is not limited to, the attachment or association of this polymer into the latex for methods including, but not limited to, adsorbing or grafting the sterically bulky polymer onto the latex surface. For example, polyvinyl alcohol can be incorporated into the latex in this manner. This sterically stabilizing component can encompass a nonionic monomer or nonionic polymer which incorporate steric stabilization to the latex particle without affecting the deposition characteristics of the anionic polymer latex.
Exemplary monomers that can be used as sterically bulky ethylenically unsaturated third monomers include, but are not limited to, those ethylenically unsaturated monomers that contain alkoxylated (for example, ethoxylated or propoxylated) functionalities. In one aspect, examples of such monomers include, but are not limited to, at least one a sterically bulky ethylenically unsaturated compound selected independently from the following:
a) CH 2 ═C(R 1A )COO(CH 2 CHR 2A O) m R 3A , wherein R 1A , R 2A , and R 3A can be selected independently from H or an alkyl group having from 1 to 6 carbon atoms, inclusive, and m can be an integer from 1 to 30, inclusive. In this aspect, R 1A , R 2A , and R 3A can also be selected independently from H or methyl, m can be an integer from 1 to 10, inclusive;
b) CH 2 ═C(R 1B )COO(CH 2 CH 2 O) n (CH 2 CHR 2B O) p R 3B , wherein R 1B , R 2B , and R 3B can be selected independently from H or an alkyl group having from 1 to 6 carbon atoms, inclusive, and n and p can be integers selected independently from 1 to 15, inclusive. Also in this aspect, R 1B , R 2B , and R 3B can be selected independently from H or methyl, and n and p can be integers selected independently from 1 to 10, inclusive;
c) CH 2 ═C(R 1C )COO(CH 2 CHR 2C O) q (CH 2 CH 2 O) r R 3C , wherein R 1C , R 2C , and R 3C can be selected independently from H or an alkyl group having from 1 to 6 carbon atoms, inclusive, and q and r can be integers selected independently from 1 to 15, inclusive. Further to this aspect, R 1C , R 2C , and R 3C can be selected independently from H or methyl, and q and r can be integers selected independently from 1 to 10, inclusive; or
d) any combination of any of these compounds.
In another aspect of this invention, a number of other types of unsaturated compounds can be used as sterically bulky ethylenically unsaturated third monomers include, but are not limited to, polymerizable surfactants. Thus, further examples of suitable sterically bulky ethylenically unsaturated third monomers include, but are not limited to, alkoxylated monoesters of a dicarboxylic acid; alkoxylated diesters of a dicarboxylic acid; alkyl allyl sulfosuccinate salts; vinyl sulfonate salts; polyoxyethylene alkylphenyl ethers such as NOIGEN RN™; polyoxyethylene alkylphenyl ethers ammonium sulfate such as HITENOL BC™; or any combination thereof. In this aspect, for example, ethoxylated mono- and diesters of diacids such as maleic and itaconic acids can also be used to achieve the desired stabilizing effect. Acrylate, methacrylate, vinyl and allyl analogs of surfactants, referred to as polymerizable surfactants, can also be used in this manner. Examples of such polymerizable surfactants include, but are not limited to, TREM LF-40™ sold by Cognis. In one aspect, these surfactants are typical in that they possess ethylenic unsaturation that allows the surfactants to be incorporated into the latex polymer itself, as well as possessing hydrophobic and hydrophilic functionality that varies. In another aspect, surfactants that are particularly applicable to the present invention include the nonionic surfactants, wherein the hydrophilic character is believed to be attributable to the presence of alkylene oxide groups. Examples of suitable nonionic surfactants include, but are not limited to, ethylene oxide, propylene oxide, butylene oxide, and the like. In such species, the degree of hydrophilicity can vary based on the selection of functionality.
The at least one sterically bulky component incorporated into the latex polymer can also constitute at least one polymer. Again, while not intending to be bound by theory, it is thought that such polymers provide steric stability to the resulting latex polymer. Such polymers are sometimes referred to in the art as protective colloids. Examples of sterically bulky polymers include, but are not limited to, polyvinyl alcohols, polyvinyl pyrollidone, hydroxyethyl cellulose, and the like, including any combination of these materials. Moreover, mixtures or combinations of any of the aforementioned sterically bulky monomers and any of these sterically bulky polymers can also be used as the at least one sterically bulky component that is incorporated into the latex polymer. A number of other monomers and polymers that can be used in the present invention that can impart stability are provided in U.S. Pat. No. 5,830,934 to Krishnan et al., the entirety of which is incorporated herein by reference.
The optional at least one sterically bulky component can be present in an amount ranging from 0 to about 25 percent by weight, based on the total weight of the monomers. In this aspect, the latex of this invention can also comprise from about 0.1 to about 20 percent, from about 0.2 to about 18 percent, from about 0.5 to about 15 percent, from about 0.7 to about 12 percent, or from about 1 to about 10 percent by weight of the sterically bulky component, based on the total monomer weight. In this aspect, Applicants' intent is to disclose individually each possible number that such a range could reasonably encompass, as well as any sub-ranges and combinations of sub-ranges encompassed therein.
Free Radical Initiators
In still a further aspect, the latex of the present invention can include a free radical initiator that can initiate the emulsion polymerization, the selection of which is known to one of ordinary skill in the art. Because the anionic latices of this invention carry a net anionic charge, when an anionic latex is prepared in the absence of the optional second anionic monomer, the overall negative charge of the latex can be supplied by the free radical initiator. Thus, in addition to an anionic monomer, the overall negative charge can be imparted to the latex by a free radical initiator, by an anionic surfactant, by an anionic sterically bulky component, or by any combination thereof. Thus, while any anionic or nonionic free radical polymerization initiator can be used, and even low levels of a cationic initiator can be tolerated, typical free radical initiators include, but are not limited to, anionic initiators including, but not limited to persulfates, peroxides, azo-based compounds, or any combination thereof, that are capable of imparting an anionic charge to the resulting latex. In this aspect, any free radical initiator which generates an anionic species upon decomposition and contributes to the anionic charge of the latex can also be utilized. Examples of such an initiator include, but are not limited to, 4,4′-azobis(4-cyano pentanoic acid), which is sold commercially as WAKO V-501™ by Wako Chemicals of Richmond, Va.
Bioactive/Antimicrobial Agents and their Incorporation
The anionic latex polymerization and encapsulation method disclosed herein can be utilized with a range of antimicrobial agents. Anionic latex polymers can also be blended with compositions containing bioactive compounds that exhibit antimicrobial activity, in order to provide a latex formulation that can be used in harsh environments where antimicrobial properties are particularly needed. In this manner, the antimicrobial properties imparted to an anionic latex by the encapsulation method disclosed herein can be supplemented with at least one antimicrobial agent in a composition that is blended with the anionic latex polymer.
In this aspect, this invention also provides methods to prepare an antifungal and antibacterial fortified anionic latex and to deposit such a latex through a wet end process onto pulp fibers, such that the resultant sheet of paper is substantially antifungal and antimicrobial. For example, in one aspect, this invention affords a method for deposition of the antimicrobial anionic latex onto pulp fibers, even though such a method is not facilitated by coulombic forces arising from opposite charges on the latex and the fibers. Thus, deposition can be carried out with an anionic latex which, although lacking inherent antimicrobial properties, will still function as a carrier for the incorporated bioactive ingredient. Such a deposition typically involves flocculation of the anionic latex using a cationic ingredient, which results in coagulation of the polymer onto the fiber, and provides a slurry of all the components that exhibits varying degrees of heterogeneity. In this aspect, the typical initiators also include azo-based compounds and compositions.
As provided herein, a wide range of polymerization conditions can be used. In one aspect, the bioactive component or additive is typically soluble in at least one of the monomers employed, and/or soluble in a monomer mixture or composition used. In another aspect, the bioactive additive can be introduced at any stage during the polymerization process including very early during the seed formation stage, including initiating the emulsion polymerization when all the components of the composition, including the at least one bioactive component, are present at the time of initiation. In another aspect, the bioadditive can be added during a later stage of polymerization process. For example, the bioactive ingredient can be introduced into the monomer feed when about 30 percent of the monomer has been fed into the polymerization reactor.
While not intending to be bound by theory, it is believed that introducing the bioactive component into the monomer feed relatively late in the polymerization process could help minimize degradation of the bioactive agent arising from the polymerization conditions. For example, it is possible that the bioactive agent could be degraded at the temperature under which polymerization is conducted, or could react with certain monomers or other components. Accordingly, to minimize any such degradation process, the bioactive agent can be added at such a time in the process, for example, when the process is more than about 50%, more than about 60%, more than about 70%, more than about 80%, or more than about 90% complete, thus minimizing the contact time between the bioactive agent and other components under the polymerization conditions. Another approach to minimize degradation of the bioactive agent is to employ bioactive agents that comprise “latent” bioactive moieties that can be activated by thermal, chemical, photochemical, or similar means, at a suitable time after the emulsion polymerization.
In another aspect of this invention, the bioactive additive can be introduced at any stage during an emulsion polymerization process, including, for example at such a time during the process at which the resulting antimicrobial latex exhibits a bioactivity that is not substantially diminished relative to a standard bioactivity exhibited by the same antimicrobial latex prepared by adding the bioactive component when the emulsion polymerization is about 50% complete. Thus, this standard bioactivity is the activity of the same antimicrobial latex synthesized from the same bioactive component and the same latex at substantially the same concentrations, prepared by adding the bioactive component when the emulsion polymerization is about 50% complete, as evaluated under similar conditions. The term “not substantially diminished” is used to refer to any difference in activity of the resulting bioactive latex, relative to this standard bioactivity, that meets any one, or more than one, of the following criteria: 1) the measured activity of the resulting bioactive latex is less than or equal to about 15% lower than the measured activity of the standard; 2) the activity of the resulting bioactive latex has a numerical activity rating based on an arbitrary activity scale that is less than or equal to about 35% lower than the numerical activity rating of the standard; or 3) the empirically-based descriptive rating of the activity level of the resulting bioactive latex is no more than two descriptive rating levels lower than the activity rating level of the standard. The measurement of antimicrobial activity can be determined according to any one, or more than one, of the following test standards: ASTM E2180-01; ASTM E2149-01; ASTM E1882-05; ASTM D3273; AATCC Test Method 30, Part 3; AATCC Test Method 100; ASTM D5590. An example of criterion 1) of “not substantially diminished” is as follows. A bioactive additive can be introduced at a time, or introduction can be initiated at a time, during an emulsion polymerization process so as to provide a resulting antimicrobial latex having a minimum inhibitory concentration (MIC) of 0.009 mg/mL, which is less than 15% lower than a MIC of 0.010 mg/mL for the standard. An example of criterion 2) of “not substantially diminished” is as follows. The bioactive additive can be introduced at a time, or introduction can be initiated at a time, during an emulsion polymerization process so as to provide a resulting antimicrobial latex having numerical activity rating of bioactivity based on an arbitrary activity scale of 5, which is less than 35% lower than the numerical activity rating of bioactivity of 7 for the standard. An example of criterion 3) of “not substantially diminished” is as follows. In an empirically-based descriptive rating system that includes contiguous rating levels of “excellent activity,” “very good activity,” and “good activity,” the bioactive additive can be introduced at a time, or introduction can be initiated at a time, during an emulsion polymerization process so as to provide a resulting antimicrobial latex having an activity rating of “good activity,” as compared to an activity rating of “excellent activity” for the standard. In any of these measurements of activity, the bioactive additive can be introduced at any time during the polymerization process that provides this result, or introduction can be initiated at a time during the polymerization process that provides the result disclosed above.
In another aspect, it is not necessary to introduce the bioactive component into the monomer feed relatively late in the polymerization process. For example, the bioadditive agent can also be added when about 0 percent, about 10 percent, about 20 percent, about 30 percent, about 40 percent, about 50 percent, about 60 percent, about 70 percent, about 80 percent, about 90 percent, or about 100 percent of the monomer has been fed into the polymerization reactor. In this aspect, the emulsion polymerization is initiated at a time when all components of the composition are not present from the time of initiation, but some are added at various times after initiating the polymerization, including, but not limited to, the at least one bioactive component. Also in this aspect, the Applicant's intent is to disclose any and all ranges between such numbers, and to claim individually each possible number that such ranges could reasonably encompass, as well as any sub-ranges and combinations of sub-ranges encompassed therein.
In another aspect, polymerization can be effected at a range of temperatures, typically selected between the lowest temperature that affords reasonable polymerization rates, and the highest temperature allowable that does not result in substantial degradation or decomposition of the antimicrobial bioactive ingredient. In one aspect, the polymerization can be carried out at the lowest temperature possible such that polymerization proceeds. In this case, the polymerization temperature should be sufficiently low to not substantially degrade or decompose any bioactive ingredient that is incorporated, yet high enough such that polymerization rates and times are adequate for useful production of the final latex polymer.
The antimicrobial agent can also be fed as a pre-emulsion made by emulsifying a mixture of monomer, additive, surfactants, water, and the like, using methods and materials known to one of ordinary skill in the art. For example, In this aspect, the dispersions can be made, among other ways, by using a relatively concentrated amount of the additive and dispersing by using surfactants, dispersants, and the like, and typically employing a mixing device such as a high speed mixer, a homogenizer, an Eppenbach mixer, or similar devices. Moreover, any other conceivable process or process known to one of ordinary skill that provides emulsion polymers in which the additive is a dispersion, an emulsion, a suspension, or the like, or substantially dissolved in the monomer mixture prior to polymerization, can be utilized.
In one aspect, useful antimicrobial agents that provide antifungal and antibacterial properties can be, in many cases, susceptible to oxidation or reduction, especially when exposed to higher temperatures. Therefore in addition to antimicrobial agent solubility, another aspect of selecting and incorporating antimicrobial agents is diminishing any oxidation or reduction reaction that would degrade such components. The processes of this invention can typically achieve this result by controlling the polymerization temperature, adjusting the time period that the active ingredient is added into the reaction to control exposure to the polymerization temperature, by adding an appropriate oxidant or reductant at some time during the polymerization to diminish or moderate any redox degradation, or any combination of these methods.
In a further aspect of the present invention, the at least one bioactive component can be selected independently from undecylenic acid; undecylenic alcohol; the reaction product of undecylenic acid with hydroxylethyl(meth)acrylate or polyethylene glycol(meth)acrylate; the reaction product of undecylenic alcohol with (meth)acrylic acid, maleic anhydride, or itaconic acid; or any combination thereof. Additional antimicrobial components that can be used in the present invention are provided in U.S. Patent Application Publication Number 2005/0003163, to Krishnan, which is incorporated herein by reference in its entirety. Another aspect of this invention provides that the at least one bioactive component can be selected independently from copper, copper salts, silver, silver salts, zinc, zinc salts, silver oxide, zinc oxide, chlorhexidine, chlorhexidine gluconate, glutaral, halazone, hexachlorophene, nitrofurazone, nitromersol, povidone-iodine, thimerosol, C 1 - to C 5 -parabens, hypochlorite salts, clofucarban, clorophene, poloxamer-iodine, phenolics, mafenide acetate, aminacrine hydrochloride, quaternary ammonium salts, oxychlorosene, metabromsalan, merbromin, dibromsalan, glyceryl laurate, pyrithione salts, sodium pyrithione, zinc pyrithione, (dodecyl)(diethylenediamine)glycine, (dodecyl)(aminopropyl)glycine, phenol, m-cresol, n-cresol, p-cresol, o-phenyl-phenol, resorcinol, vinyl phenol, polymeric guanidines, polymyxins, bacitracin, circulin, octapeptins, lysozmye, lysostaphin, cellulytic enzymes, vancomycin, ristocetin, actinoidins, avoparcins, tyrocidin A, gramicidin S, polyoxin D, tunicamycin, neomycin, streptomycin, or any combination thereof.
Yet another aspect of this invention provides that the at least one bioactive component can exhibit fungicidal activity. In this aspect, suitable fungicides that are applicable to this disclosure include, but are not limited to, azoles, quaternary ammonium compounds, dithiocarbamates, dicarboximides, or any combination thereof. For example, in this aspect, an azole fungicide can be selected from azaconazole, biternatol, bromuconazole, cyproconazole, diniconazole, fenbuconazole, flusilazole, flutnafol, imazalil, imibenconazole, metconazole, paclobutrazol, perfuazoate, penconazole, simeconazole, triadimefon, triadimenol, uniconazole, or any combination thereof. Also in this aspect, a dithiocarbamate fungicide can be selected from mancozeb, maneb, metiram, zineb, or any combination thereof.
In another aspect, suitable fungicides can include, but are not limited to, fludioxonil, fluquinconazole, difenoconazole, 4,5-dimethyl-N-(2-propenyl)-2-(trimethylsilyl)-3-thiophenecarboxamide(sylthiopham), hexaconazole, etaconazole, triticonazole, flutriafol, epoxiconazole, bromuconazote, tetraconazole, myclobutanil, bitertanol, pyremethanil, cyprodinil, tridemorph, fenpropimorph, kresoxim-methyl, azoxystrobin, ZEN90160™, fenpiclonil, benalaxyl, furalaxyl, metalaxyl, R-metalaxyl, orfurace, oxadixyl, carboxin, prochloraz, triflumizole, pyrifenox, acibenzolar-S-methyl, chlorothalonil, cymoxanil, dimethomorph, famoxadone, quinoxyfen, fenpropidine, spiroxamine, triazoxide, BAS50001F™, hymexazole, pencycuron, fenamidone, guazatine, and the like, including any combination thereof. Still another aspect of this invention provides that suitable fungicides can include, but are not limited to, benomyl (also known as benlate), captan, carbendazim, capropamid, ethirimol, flutolanil, fosetyl-aluminum, fuberidazole, hymexanol, kasugamycin, iminoctadine-triacetate, ipconazole, iprodione, mepronil, metalaxyl-M (mefenoxam), nuarimol, oxine-copper, oxolinic acid, perfurazoate, propamocarb hydrochloride, pyroquilon, quintozene (also known as PCNB), silthiopham, MON™ 65500, tecnazene, thiabendazole, thifluzamide, thiophenate-methyl, thiram, tolclofos-methyl, triflumizole, and the like, including any combination thereof. Moreover any combination or mixture of any of these fungicides can be employed.
In yet another aspect of this invention, typical amounts of bioactive component that can be added during the emulsion polymerization can range from about 0.01 percent to about 40 percent by weight bioactive additive, based on the total monomer weight. In another aspect, typical amounts of bioactive component that can be added during the emulsion polymerization can range from about 0.025 percent to about 35 percent, from about 0.05 percent to about 30 percent, from about 0.1 percent to about 25 percent, from about 0.25 percent to about 20 percent, or from about 0.5 percent to about 15 percent by weight bioactive additive, based on the total monomer weight. In this aspect, the Applicant's intent is to disclose individually each possible number that such ranges could reasonably encompass, as well as any sub-ranges and combinations of sub-ranges encompassed therein. As compared to the amount of antimicrobial component added as a “post-add,” these concentrations of bioactive additive are typically much larger than the post-add amounts. Among other things, this features provides stable, concentrated dispersions that can be used as concentrates, as additives, or as concentrated dispersions that can be diluted and added to other systems which require antimicrobial protection.
As disclosed herein, in one aspect, the bioactive component is typically dissolved in the monomer feed during the emulsion polymerization process. Thus, the bioactive additive is typically at least partially soluble in one or more of the monomers employed. Further, the bioactive additive can be moderately soluble, substantially soluble, or highly soluble in one or more of the monomers employed. This feature can allow, among other things, the incorporation of hydrophobic bioactive ingredients, the use of high amounts and concentrations of bioactive ingredients, greater control over the antimicrobial properties including enhancing the effectiveness of the antimicrobial properties, the use of minimal amounts of surfactant, and at least partial encapsulation of the bioactive ingredient. In some instances, the latex polymer can substantially encapsulate the added bioactive component, thus the latex polymer can function as a type of carrier for the active ingredients. This process also allows for the incorporation of the antimicrobial ingredients without substantially degrading the activity of these compounds.
In another aspect, useful bioactive additives in this invention can also be water soluble to any extent, including substantially water soluble, examples of which include o-phenylphenate (deprotonated o-phenylphenol), and similar agents. Thus, it is not necessary that such a hydrophilic bioactive additive be soluble in any monomer that is to be polymerized. In still another aspect, useful bioactive additives in this invention can be substantially insoluble in the monomers being polymerized and substantially insoluble in water. In this aspect, a dispersion of the bioactive component can be made by, among other ways, by dispersing a certain concentration of the additive with the use of surfactants and the like, typically with the use of high speed mixers or homogenizers.
Because the post-added additives are typically dispersions that are post-mixed into a formulation, it can be difficult to adequately disperse the bioactive additive into the polymer film, binder, coating, or the like, in which they are used. Moreover, typical additive dispersions that are used today can cause or be associated with moisture sensitivity and leaching of the additive, and many post-adds do not persist within the product for a sufficient period of time to provide adequate antifungal protection. The approach provided in this disclosure allows the use of minimal surfactants to incorporate the bioactive additives into the latex, and because the bioactives are introduced during the polymerization, they are typically encapsulated and are not easily released from the resulting latex. As a result, there can be less leaching of the bioactive component, and better overall distribution of the bioactive ingredient throughout the polymer film, binder, coating, and the like. Accordingly, this method can provide a potentially safer and more environmentally friendly dispersion, while also offering sustained antifungal or antibacterial protection.
The process disclosed herein also allows the latex to be used as a concentrate, in contrast to the typical concentrate dispersions that are not as stable as those provided herein. As a result, the typical concentrate dispersions are not as easily manipulated and therefore cannot be incorporated as easily into a finished product, and can have deleterious effects on performance, such as water sensitivity, if dosage is increased. A concentrate of the latex provided herein can be diluted and used with or without other materials if such materials are needed to provide an adequate level of additive. Intimate incorporation of an active ingredient in this manner can afford a homogeneous distribution of the additive and result in superior and sustained performance compared to a pre-made dispersions. An additional benefit of this intimate incorporation of the bioactive agent is apparent in films that are prepared using these latices, which are observed to be substantially transparent. This feature highlights the highly homogeneous assimilation of the bioactive agent into the latex particles and how this uniform distribution can provide useful properties for applications such as transparent bioactive films and the like, even in relatively high concentrations such as up to about 20 percent to about 25 percent.
Other Additives
In another aspect of this disclosure, the latex provided herein can also include other additives to improve the physical and/or mechanical properties of the polymer, the selection of which are known to one skilled in the art. Such additives include, for example, processing aids and performance aids, including but are not limited to, cross-linking agents, natural or synthetic binders, plasticizers, softeners, foam-inhibiting agents, froth aids, flame retardants, dispersing agents, pH-adjusting components, sequestering or chelating agents, or other functional components, or any suitable combination thereof.
Exemplary Substrates and Applications for Bioactive Anionic Polymer Latices
The deposition of the latex polymer coatings of this disclosure on any number of different substrates, such as textiles, metal, cellulosic materials, plastics, and the like, can impart desired end-use performance properties to those materials, and therefore tailor the substrates for a range of applications. For example, in one aspect, the present disclosure provides a treated fibrous material which can comprise at least one fiber and at least one bioactive anionic polymer latex as provided herein. In one aspect, the treated fibrous material can comprise at least one fiber and at least one bioactive anionic polymer latex deposited on, or associated with, the at least one fiber. If desired, the bioactive anionic polymer can be applied to the fiber in the form of a powder, or the polymer composition can be deposited on the fiber by any suitable method known to the skilled artisan.
As used herein, the term “fiber” is intended to be broadly construed and can include single or multiple filaments that can be present in a variety of ways. It should be appreciated that only a single fiber can be treated with the bioactive anionic polymer latex of the invention if so desired. Fibers that can be used in conjunction with this invention can encompass natural fibers, synthetic fibers, or any combination or mixture thereof. Natural fibers include, but are not limited to, animal fibers (for example, silk and wool); mineral fibers (for example, asbestos); and vegetable-based fibers (for example, cotton, flax, jute, and ramie). Synthetic fibers include, but are not limited to, those made from polymers such as polyamides, polyesters, acrylics, and polyolefins. Other examples of fibers include, but are not limited to, rayon and inorganic substances extruded in fibrous form such as glass, boron, boron carbide, boron nitride, carbon, graphite, aluminum silicate, fused silica, and metals such as steel. In another aspect, cellulosic or wood fibers also can be treated with the bioactive anionic polymer latex of the invention if so desired. Recycled fibers using any suitable fiber such as the above materials may also be employed. Any mixture of fibers can be treated with the bioactive anionic polymer latex of the invention if so desired.
The treated fibrous material can, in another aspect, have at least one other polymeric layer deposited on the fiber so as to form a composite fibrous structure, thus multiple polymeric layers of various types can be used if desired. For example, anionic polymer latices may be deposited on the treated fibrous material to enhance specific properties of the treated fibrous material. In another aspect, the fibrous material can be treated in a sequential fashion using, alternately, bioactive anionic polymer latices and cationic polymer latices, to form multiple layered structure. While not intending to be bound by theory, it is thought that simple coulombic interactions between anionic and cationic polymers enhance the stability of such structures, leading to treated fibrous materials that are robust. Layers of various other non-bioactive polymers can be employed similarly, for example, deposited on the anionic polymer latex which is present on the fibrous material to form a composite structure. In this fashion, unique layering architecture can be constructed with specially modified surfaces in accordance with this invention.
In a further aspect, the present invention also provides an article of manufacture comprising a substrate and a bioactive anionic polymer latex deposited or positioned thereon, as provided herein. For the purposes of this disclosure, the term “substrate” is intended to be construed and interpreted broadly to include all those formed from inorganic materials, organic materials, composites thereof, mixtures thereof, or any type combination thereof. For example, the substrate can encompass, but is not limited to, paper, composites, fibers, fillers, pigments, and the like, as well as other organic and inorganic materials.
In one aspect of this invention, as disclosed herein, a fibrous substrate can be employed. The term “fibrous substrate” is also intended to be construed and interpreted broadly to include at least all the fibers, woven textiles, and non-woven textiles disclosed herein. Thus, the fibrous substrate may be present, for example, in the form of a web, a yarn, a fabric, a textile substrate, and the like. Further examples of fibrous substrates include, but are not limited to, natural fibers such as cotton and wool to synthetic fibers such as nylon, acrylics, polyesters, urethanes, and the like. Known application processes can be used to apply the bioactive anionic polymer latex, such as rod/knife coating, impregnation, back coatings, printing, as pretreatments on individual fibers, or as a finished good. Also as used herein, the term “textile substrate” can be defined according to its use in U.S. Pat. No. 5,403,640 to Krishnan et al., the disclosure of which is incorporated herein by reference in its entirety. In this aspect, for example, “textile substrate” can encompass a fiber, a web, a yarn, a thread, a sliver, a woven fabric, a knitted fabric, a non-woven fabric, an upholstery fabric, a tufted carpet, a pile carpet, and the like, including any combination thereof, formed from any of the fibers described herein.
The bioactive anionic latex composition of this invention also can be applied to a wide variety of plastic or rubber substrates. Examples of such materials include, but are not limited to, commodity molded thermoplastics such as polyolefins; engineering thermoplastics such as polysulfones, acetals, polycarbonates, and the like; thermosets such as epoxies, urethanes, and related materials; and as extruded or blown films. The polymer could be applied as a coating on the surface by rod/knife coating, spray, dipping, as a laminate coating during the extrusion process, or as a coating applied in the mold during the molding process. Rubber products would include sheets, extruded/molded articles, composites, and the like. In another aspect, the bioactive anionic latex compositions of this invention also can be deployed in solid form. In this aspect, for example, the inventive latices can be coagulated or spray dried to provide the solid bioactive anionic latex, which can be employed in solid form as an additive in plastic products, in processes such as extrusion or blow molding, as additives for various polyethylenes, polypropylenes, and the like, and in any number of other polymer and plastic applications.
The bioactive anionic latex composition of this invention also can be applied to wood or metal substrates. In this aspect, suitable substrates would include all kinds of natural and engineered wood substrates. Suitable metal substrates would include both metals and metal alloys, such as carbon steel, stainless steel, and including solid steel bars, sheets, coils, ropes, and such, wherein the composition is applied as a coating by one of the numerous processes such as spraying dipping, brushing, roller coating, and related methods.
In this context, an article of manufacture comprising a substrate and a bioactive anionic polymer latex deposited or positioned thereon can be made in accordance with standard procedures known to one of ordinary skill in the relevant art. The article of manufacture can have, in another aspect, at least one other polymeric layer deposited thereon so as to form a composite structure, thus multiple polymeric layers of various types can be used if desired. For example, other layers of various polymers can be deposited on the bioactive anionic polymer latex which is present in the article of manufacture to form a composite structure. In this aspect, deposition of a bioactive anionic latex can be followed by the deposition of a cationic latex or other polymers to enhance specific properties of the article of manufacture. Thus, uniquely tailored articles with specially modified surfaces can be made in accordance with the present invention.
In a broader aspect, the present invention also provides a coated material comprising any material and a bioactive anionic polymer latex deposited or positioned thereon, wherein additional layers of other materials optionally can be used in combination with the bioactive anionic polymer latex of this invention. As used herein, the term “material” is intended to be used broadly to include, but not be limited to, any inorganic material, any organic material, any composite thereof, or any combination thereof. Examples of suitable materials include, but are not limited to, a fiber, a filler, a particle, a pigment, composites thereof, combinations thereof, mixtures thereof, and the like.
A multiple deposition process can also be used to make composite films that have applications in areas other than textiles and fibrous materials. In one aspect, for example, the bioactive anionic polymer latex of this invention can be used to fabricate multilayer elastomeric gloves. Cellulosic structures can also be made using the bioactive anionic polymer latex provided herein including, but not limited to, cellulosic composites and heavy duty cellulosic structures. Examples of cellulosic composites include, but are not limited to, those composites relating to filtration, shoe insoles, flooring felt, gasketing, and the like. Heavy duty cellulosic structures include, but are not limited to, dunnage bags, industrial wipes, and related structures. In a further aspect, the deposition process and bioactive anionic polymer latex of this invention also can be used in other technology arts including, but not limited to, anionic flocculants, wet and dry strength additives for papermaking, anionic retention aids, cement modifications, dye fixation, redispersible powders, and the like.
The present invention can afford certain advantages as compared to previous methods used to fabricate bioactive materials. In one aspect, for example, the bioactive anionic latices can be substantially deposited on a substrate such that residual bioactive latex does not remain in the processing fluid medium, providing a potential advantage from an environmental standpoint. Moreover, bioactive anionic latices can be preferentially deposited on any substrate that carries a net positive charge, and deposition can occur in a uniform manner, thereby using less latex. In this aspect, and while not intending to be bound by theory, the bioactive anionic latices are thought to be capable of forming substantially uniform monolayers of polymer material on a positively charged substrate, thereby allowing the use of less latex to provide the desired coverage. Because the bioactive anionic latices can be formed by existing emulsion polymerization processes, the polymerization methods advantageously allow for the preparation of high molecular weight polymers.
In a further aspect, the antimicrobial anionic polymer latices of this disclosure can constitute a useful component of filled latex. Many fillers such as mica or calcium carbonate are negatively charged and can be difficult to use in large amounts in combination with cationic latices. Thus, when a filled latex is desired, this invention affords, among other things, an anionic latex polymer that can be used to prepare a filled latex, even when relatively high concentrations of fillers are needed.
As provided herein, the latex composition of the present invention can be applied to a wide variety of substrates using various techniques that are well known to one of ordinary skill in the art. As a result, there are numerous applications for the present invention, many of which are provided in the following listing. In this aspect, while this listing is not comprehensive, specific applications include, but are not limited to: textiles such as residential and commercial carpets or tiles; liquid and air filters for HVAC or vacuum cleaners, or automotive uses; medical surgical gowns, drapes, dressings, covers, and the like; pretreatment for fibers, printed or dyed fabrics for apparel, furnishings, sheets, towels, and the like; diapers and incontinence articles; interior automotive applications such as trim, upholstery, mats, filters, and such; upholstery coatings; laminating and bonding adhesives; foams for sound absorbency; foamed articles such as pillows and mattresses; belting or other machinery parts for food handling and the like; tapes such as masking tapes, surgical tape, industrial tapes, and the like; electrical, industrial, and household cleaning wipes, cloths, and sponges; shoe products such as insoles, box toes, and such; plastic and/or rubber items such as tool handles, tool grips, toys, rubber gloves, sheets, or other articles; machinery housing such as for computers, display and diagnostic devices or instrumentation; medical devices such as catheters, balloons, tubing, syringes, diagnostic kits, and the like; packaging or product protection, as applied to perishables, computer peripherals, semiconductors, memory chips, CDs, DVDs, and the like; impact modifiers for acrylics, polycarbonates, and such; overdips or underdips for gloves such as gloves for clean rooms; breathable films; antipenetrant for fabric supported gloves; cutting boards; extruded and blown films for packaging; paper products such as vacuum bags, book covers, air filters, liquid filters, wallcoverings, wet and dry wipes, tissues, and such; felt for vinyl floor coverings; molded pulp applications; packaging such as boxes, cartons, molded articles, and related items; size press coatings for gift wraps, ink jet media, breathable coatings, and the like; wet end additives in paper, tapes, labels for use in masking, surgical applications, general purpose applications, and such; binders for use in paper; binders for use in wallboard such as gypsum wallboard and the like; adhesives for use in tapes, labels, decals, films, book bindings, pressure sensitive applications, flexible packaging and laminating adhesive (FPLA), and the like; inorganic and/or organic materials such as coating or encapsulation of fillers or pigments, construction sealers and grouts, gypsum wallboard coatings or binders, exterior or interior coatings, and the like; tile adhesives; floor coatings for use in hospitals, clean rooms, clinics, schools, and related environments; coatings for hospital and medical environments; ceiling tiles; glass fiber coatings such as glass mats, insulation, filter materials, reinforced composites, and such; coatings for air conditioning or refrigeration coils; other components for air conditioning systems, heat exchangers, ion exchangers, process water systems including cooling water treatment, solar-powered units, coated pipes, and the like; kitchen items; components of sanitary equipment; components of water systems; operator units of devices such as touch panels; materials used in bathrooms such as shower curtains, fixtures, toilet items, and even jointing or sealing compounds; medical devices such as use in coatings for stents, implants, prostheses, catheters, tubing, contact lenses, protective or backing films, medical instruments, and other medical devices for providing the sustained action of bioactive agents; articles which are contacted by large numbers of people such as telephone handsets, stair rails, door handles, window catches, grab straps and grab handles in public conveyances, and the like; liquid disinfectants and cleaners; personal care or hygiene products such as shampoos, lotions, creams, hair and skin care products, body wash, cosmetics, toilet items, and the like; hygiene coatings of surfaces other than floors, such as in hospitals, clinics, schools, homes, offices, and the like; hard and porous surface coatings as applicable to walls, ceilings, floors, counter tops, and the like; decorative concrete; wood such as oriented strand board (OSB) coatings; decking and construction materials for coating or impregnation; composite construction materials; furniture coatings; hygiene coatings such as used in table tops, counter tops, door knobs, door handles, fixtures, and the like; flooring applications such as in laminates, hardwood flooring, and other composite flooring materials; decorative laminates such as table tops, counter tops, furniture, and the like; other construction materials such as roofing material, wall material, facades, fencing, or for wood protection applications; marine applications such as in boat hulls, docks, buoys, drilling platforms, or ballast water tanks; metal such as cabinets, door knobs, handles, fixtures, and such; and furniture, coatings as applicable to appliances, original equipment manufacture (OEM), and the like.
In this aspect, the antimicrobial formulations of the invention can be useful as a biofouling inhibitor, in particular, in cooling circuits. To prevent damage to cooling circuits by infestation with algae or bacteria, the circuits typically have to be cleaned frequently or be appropriately oversized. In the open cooling systems usually found in power plants and in chemical plants, the addition of microbiocidal substances, such as formalin, is generally not possible. Other microbiocidal substances are frequently highly corrosive or form foams, preventing their use in systems of this type. Deposition of bacteria or algae on components of the system can thus be effectively inhibited. Therefore, the formulations and materials of this invention can be quite useful in such applications.
In another aspect, the present invention can also provide a process for sterilizing cooling-water streams or process water systems, by adding antimicrobial formulations in dispersed form to the cooling water. The dispersed form can be obtained in the preparation process itself, for example, by emulsion polymerization as detailed herein, but also by precipitation polymerization, or suspension polymerization, or subsequently by milling of the antimicrobial polymer obtained by any of these methods, for example, in a jet mill.
The antimicrobial latex polymer of this invention can be applied or used as a coating composition, which can be used for a wide variety of purposes in connection with which antimicrobial action is desired. For example, in one aspect, the antimicrobial latex polymers disclosed herein can be used in connection with a wide range of insulating materials such as wrapping materials for pipes, which are a particular risk of bacterial attack. Thus, the materials of the invention are useful when used in connection with elastomeric insulating materials. Such coating compositions can also be used in connection with industrial insulation, such as is used for insulating pipelines, examples being heating pipes, and for insulating valves and ducts. Moreover, antimicrobial latices disclosed herein can be used in conjunction with all thermal and/or acoustic insulations and related insulating materials for numerous end applications. The latices provided herein can also be used in conjunction with industrial foams and foam materials as substrates for antimicrobial coatings. Such coatings comprising the antimicrobial latices disclosed herein also can be used as coatings for air-conditioning plants, condensers, refrigerators and other refrigeration units, and also parts thereof, and also for coating compositions as paints for marine craft and for wood preservation. Coatings comprising the antimicrobial latices of this disclosure can also be employed as the coating of substrates such as metal, plastic, or ceramic, in hygiene installations, hospitals, or in the food industry, or any articles involving frequent contact of any type which may easily transmit infection pathogens, such as door handles, sanitary fittings, switches, and grips. In the case of such coatings the use of a coating composition in the form of powder coatings can be advantageous.
Applications of Antimicrobial Latices to Medical Devices
The term “medical device” as used herein refers to any material, natural or artificial, that is inserted into a mammal. Particular medical devices suited for application of the antimicrobial latices and compositions of this invention include, but are not limited to, peripherally insertable central venous catheters, dialysis catheters, long term tunneled central venous catheters, long term non-tunneled central venous catheters, peripheral venous catheters, short-term central venous catheters, arterial catheters, pulmonary artery Swan-Ganz catheters, urinary catheters, artificial urinary sphincters, long term urinary devices, urinary dilators, urinary stents, other urinary devices, tissue bonding urinary devices, penile prostheses, vascular grafts, vascular catheter ports, vascular dilators, extravascular dilators, vascular stents, extravascular stents, wound drain tubes, hydrocephalus shunts, ventricular catheters, peritoneal catheters, pacemaker systems, small or temporary joint replacements, heart valves, cardiac assist devices and the like and bone prosthesis, joint prosthesis and dental prosthesis.
In one aspect, the medical devices that can be used in conjunction with the bioactive anionic latices of this invention include, but are not limited to, non-metallic materials such as thermoplastic or polymeric materials. Examples of such materials include rubber, plastic, polyethylene, polyurethane, silicone, G ORTEX ™ (polytetrafluoroethylene), D ACRON ™ (polyethylene tetraphthalate), polyvinyl chloride, T EFLON ™ (polytetrafluoroethylene), elastomers, nylon and D ACRON ™ sealed with gelatin, collagen or albumin. The amount of each bioactive anionic latex used to coat the medical device varies to some extent, but is at least a sufficient amount to form an effective concentration to inhibit the growth of bacterial and fungal organisms.
The antimicrobial latices can be used alone or in a combination comprising two or more antimicrobial latices. Each antimicrobial latex can comprise one or more antimicrobial components as provided herein. Any application or use disclosed herein can further encompass the use of at least one bioactive latex in conjunction with at least one other antimicrobial agent that can be dispersed throughout the surface of the medical device. The amount of each bioactive latex and each antimicrobial agent used to impregnate the medical device varies to some extent, but is at least of an effective concentration to inhibit the growth of bacterial and fungal organisms.
In one aspect, the antimicrobial agent can be selected from an antibiotic, an antiseptic, a disinfectant, or any combination thereof. In another aspect, the antimicrobial agent can be an antibiotic including, but not limited to, penicillins, cephalosporins, carbepenems, other beta-lactam antibiotics, aminoglycosides, macrolides, lincosamides, glycopeptides, tetracylines, chloramphenicol, quinolones, fucidins, sulfonamides, trimethoprims, rifamycins, oxalines, streptogramins, lipopeptides, ketolides, polyenes, azoles, echinocandins, or any combination thereof.
In one aspect, at least one drug can be applied to a medical device using bioactive latices provided herein, and used in combinations with drugs that can adhere to, rather than be encapsulated by, the bioactive latices. For example, a anionic antimicrobial latex coating can be applied as a coating to a medical device that can have an ionic charge. Subsequently, drugs having a complimentary charge can be applied to, and can bind to, the charged coating applied to the surface of device when the charged coating and the drug are exposed to one another. The strength of bonding between the drug and the coating can be used to influence how readily the drug can be released from the surface of the device. In one aspect, this disclosure provides for delivering an implant or medical device having this drug delivery feature to a selected anatomical site. In this aspect, typically drugs that are useful include, but are not limited to, antimicrobials and antibiotics such as neomycin and sulfa drugs, anti-inflammatory agents such as steroidal or non-steroidal anti-inflammatory agents, or combinations thereof.
Applications of Bioactive Anionic Polymer Latices in Wallboard Manufacture
Wallboard is typically produced by enclosing a core of an aqueous slurry prepared using calcium sulfate hemihydrate, referred to as calcined gypsum, and other materials between two large sheets of wallboard cover paper. After the gypsum slurry has set and has been dried, the formed sheet is cut into standard sizes. Thus, the core of wallboard can be considered to be prepared by combining a “dry” portion and a “wet” or aqueous portion which is then situated between two sheets of cover paper, and which sets or hardens.
A major “dry” ingredient of the gypsum wallboard core is calcium sulfate hemihydrate, commonly referred to as calcined gypsum or stucco, which is prepared by drying, pulverizing, and calcining natural gypsum rock (calcium sulfate dihydrate). The drying step simply removes any free moisture that is not chemically bound in the rock, while calcining liberates a portion of the chemically bound water molecules. As a result, calcined gypsum has the desirable property of being chemically reactive with water, and will set rather quickly when the two are contacted and the calcium sulfate hemihydrate is rehydrated to its dihydrate state. In addition to calcium sulfate hemihydrate, the dry ingredients can include a wide range of addititives, such as set retarders, set accelerators, antidesiccants, stabilizers, starch, and/or other additives that can be useful in the production process or the final wallboard properties.
In addition to including water, the “wet” portion of the wallboard core composition comprises paper pulp. In one aspect, the wet portion of the wallboard core composition typically, though not necessarily, includes a first wet component and a second wet component. The first wet component can be referred to as a paper pulp solution, and includes a mixture of water, paper pulp, optionally one or more fluidity-increasing agents, and optionally a set retarder. The paper pulp solution provides a major portion of the water that forms the gypsum slurry of the core composition. The second wet component can include a composition comprising strengthening agents, foaming agents, surfactants, other conventional additives, or any combination thereof. Any wet component generally, or the first wet component and second wet component, can be combined with the dry portion of the gypsum wallboard core in any order or manner.
In another aspect, the face paper and backing paper cover sheets used in wallboard manufacture are typically multi-ply paper manufactured from re-pulped newspapers. Both the face paper and the backing paper usually have an inner ply (typically unsized) which contacts the core slurry such that gypsum crystals can grow up to or into the inner ply. This gypsum crystal-paper interaction constitutes one principal form of bonding between the core slurry and the cover sheet. The middle plies are usually sized and an outer ply is more heavily sized and can be treated to control the absorption of paints and scalers. Both cover sheets typically have sufficient permeability to allow for water vapor to pass through during the downstream board drying process. These and related methods for the production of gypsum wallboard generally are described, for example, in Michelsen, T. “Building Materials (Survey),” Kirk - Othmer Encyclopedia of Chemical Technology , (1992 4 th ed.), vol. 4, pp. 618-619, the disclosure of which is hereby incorporated herein by reference.
One aspect of this invention provides an antimicrobial wallboard article of manufacture comprising at least one bioactive latex polymer disclosed herein, and also provides a process for making an antimicrobial gypsum wallboard comprising at least one bioactive latex polymer. In this aspect, the bioactive latex polymer can be used in any component of the wallboard, that is, as a component of the gypsum wallboard core, the first cover sheet, the second cover sheet, or any combination thereof. Thus, this method and article comprise adding at least one antimicrobial latex to the wallboard or any component thereof, at levels sufficiently effective against microbes, therefore, a bioactive latex is an optional ingredient of each wallboard component. Moreover, the at least one bioactive latex polymer can be used in any form, such as an emulsion, a dispersion, or in solid form, as disclosed herein. Thus in a further aspect, this disclosure provides for adding the at least one bioactive latex polymer in a finishing step such as coating, spraying, painting, or the like.
In a further aspect, this invention also provides for using bioactive anionic polymer latices as binder or coating materials that can be combined with paper pulp used to prepare the face paper and backing paper cover sheets in wallboard manufacture. In this aspect, either or both sheets of the wallboard cover paper can comprise at least one bioactive anionic polymer latex disclosed herein, which can be the same or can be different. These bioactive anionic latices can be used to prepare the inner, middle, or outer plies of the cover sheets, or any combination thereof. Moreover, any combination of cover sheets in which the first, the second, or both covers sheets comprise antimicrobial components can be used with a gypsum slurry that comprises at least one bioactive anionic polymer latex, or with a gypsum slurry that does not comprise at least one bioactive anionic polymer latex.
Thus in one aspect, this disclosure provides a method of making an antimicrobial wallboard comprising:
a) forming a slurry comprising calcium sulfate hemihydrate, water, paper pulp, and optionally at least one first bioactive anionic polymer latex;
b) depositing the slurry onto a first cover sheet optionally comprising at least one second bioactive anionic polymer latex; and
c) applying a second cover sheet optionally comprising at least one third bioactive anionic polymer latex on top of the deposited slurry; and
d) drying the resulting wallboard;
wherein at least one of the slurry, the first cover sheet, or the second cover sheet comprises at least one bioactive aionic polymer latex; and
wherein the at least one first bioactive anionic polymer latex, the at least one second bioactive anionic polymer latex, and the at least one third bioactive anionic polymer latex are the same or are different.
Thus, the at least one first, the at least one second, and at least one third bioactive anionic polymer latices are selected independently of each other. Any of the bioactive anionic polymer latices or combinations of bioactive anionic polymer latices disclosed herein can be employed in any of the antimicrobial wallboard components.
Accordingly, this invention also provides an antimicrobial wallboard comprising:
a) a gypsum sheet optionally comprising at least one first bioactive anionic polymer latex;
b) a first cover sheet disposed on one side of the gypsum sheet and optionally comprising at least one second bioactive anionic polymer latex; and
c) a second cover sheet disposed on the opposite side of the gypsum sheet and optionally comprising at least one third bioactive anionic polymer latex;
wherein at least one of the gypsum sheet, the first cover sheet, or the second cover sheet comprise at least one bioactive anionic polymer latex; and
wherein the at least one first bioactive anionic polymer latex, the at least one second bioactive anionic polymer latex, and the at least one third bioactive anionic polymer latex are the same or are different.
Although any methods, devices, and materials similar or equivalent to those described herein can be used in the practice or testing of the invention, the typical methods, devices and materials are herein described. All publications and patents mentioned herein are incorporated herein by reference for the purpose of describing and disclosing, for example, the constructs and methodologies that are described in the publications, which might be used in connection with the presently described invention. The publications discussed herein are provided solely for their disclosure prior to the filing date of the present application. Nothing herein is to be construed as an admission that the inventors are not entitled to antedate such disclosure by virtue of prior invention.
When Applicants disclose or claim a range of any type, for example a range of temperatures, a range of concentrations, a range of numbers of atoms, a weight percent, or the like, Applicants' intent is to disclose or claim individually each possible number that such a range could reasonably encompass, as well as any sub-ranges and combinations of sub-ranges encompassed therein. Thus, when the Applicants disclose or claim a chemical moiety having a certain number of carbon atoms, Applicants' intent is to disclose or claim individually every possible number, sub-range, and combination of sub-ranges that such a number range could encompass, consistent with the disclosure herein. For example, the disclosure that R is selected from an alkyl group having up to 12 carbon atoms, or in alternative language a C 1 to C 12 alkyl group, as used herein, refers to an R group that can be selected independently from an alkyl group having 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, or 12 carbon atoms, as well as any range between these two numbers for example a C 3 to C 8 alkyl group, and also including any combination of ranges between these two numbers for example a C 3 to C 5 and C 7 to C 10 alkyl group. Thus, Applicants retain the right to replace the terminology such as “group having up to 12 carbon atoms” with any individual number that such a range could reasonably encompass, as well as any sub-ranges and combinations of sub-ranges encompassed therein. In another example, by the disclosure that the molar ratio typically spans the range from about 0.1 to about 1.0, Applicants intend to recite that the molar ratio can be selected from about 0.1:1, about 0.2:1, about 0.3:1, about 0.4:1, about 0.5:1, about 0.6:1, about 0.7:1, about 0.8:1, about 0.9:1, or about 1.0:1, as well as any sub-ranges and combinations of sub-ranges encompassed therein. Similarly, the disclosure that a particular weight percent can be from about 80 percent to about 90 percent by weight, Applicants' intend to recite that the weight percent can be about 80 percent, about 81 percent, about 82 percent, about 83 percent, about 84 percent, about 85 percent, about 86 percent, about 87 percent, about 88 percent, about 89 percent, or about 90 percent, by weight.
Applicants reserve the right to proviso out or exclude any individual members of any such group, including any sub-ranges or combinations of sub-ranges within the group, that may be claimed according to a range or in any similar manner, if for any reason Applicants choose to claim less than the full measure of the disclosure, for example, to account for a reference that Applicants may be unaware of at the time of the filing of the application. Further, Applicants reserve the right to proviso out or exclude any individual substituents, additives, compounds, monomers, surfactants, structures, and the like, or any groups thereof, or any individual members of a claimed group, if for any reason Applicants choose to claim less than the full measure of the disclosure, for example, to account for a reference that Applicants may be unaware of at the time of the filing of the application.
For any particular chemical compound disclosed herein, any general disclosure or structure presented also encompasses all isomers, such as conformational isomers, regioisomers, stereoisomers, and the like, that can arise from a particular set of substituents. The general structure also encompasses all enantiomers, diastereomers, and other optical isomers whether in enantiomeric or racemic forms, as well as mixtures of stereoisomers, as the context requires.
The present invention is further illustrated by the following examples, which are not to be construed in any way as imposing limitations upon the scope thereof. On the contrary, it is to be clearly understood that resort can be had to various other aspects, embodiments, modifications, and equivalents thereof which, after reading the description herein, may suggest themselves to one of ordinary skill in the art without departing from the spirit of the present invention or the scope of the appended claims.
In the following examples, unless otherwise specified, the reagents were obtained from commercial sources. General procedures, including general synthetic testing procedures for polymer latices, are provided in U.S. Patent Application Publication Numbers 2005/0065284 and 2005/0003163, to Krishnan, each disclosure of which is incorporated herein by reference in its entirety.
EXAMPLE 1
Bioactive Anionic Latex Preparation
A one-liter polymerization reactor can be charged with the following ingredients: about 270 g of water; about 6 g of the nonionic surfactant A BEX ™ 2525 (Rhodia); about 2.7 g of an anionic surfactant D OWFAX ™ 2A1 (Dow Chemical Company), and about 3 g of methacrylic acid. The reactor contents can be deoxygenated by subjecting the reactor to several vacuum/N 2 fill cycles.
The following reactor feeds can be prepared:
1) An aqueous monomer feed containing about 150 g of water, about 6 g of methoxy polyethyleneglycolmethacrylate (MPEG 550 from Cognis), about 4.5 g of methacrylic acid, about 1.3 g of D OWFAX ™ 2A1, and about 6 g of A BEX ™ 2525. The total feed time into the reactor is 5 hours;
2) A non-aqueous monomer feed containing about 153 g of butyl acrylate, about 132 g of methyl methacrylate, and about 64 g of the bioactive agent. The total feed time for this feed is 5 hours. The bioactive agent can be introduced into this feed after about a 3-hour time period. Thus, the non-aqueous monomer feed during the first 3 hours contains only butyl acrylate and methyl methacrylate; and
3) An initiator feed that can contain about 30 g of water and about 2.10 g of an initiator, V-501™ (Wako Chemical). The total feed time is about 5.5 hours. A few drops of ammonia can be added to aid in the dissolution of the initiator, if needed.
To the initial reactor charge can be added 10% of the non-aqueous monomer feed, which contains only the two monomers methyl methacrylate and butyl acrylate, as the bioactive agent is not introduced into the monomer until 3 hours into the feed. The temperature of the reactor then can be raised to about 165° F. and when this set point is reached, an original initiator solution (separate from the initiator feed described above) containing about 3 g of water and about 0.30 g of V-501 can be injected into the reactor. The reactor contents are maintained at this temperature for about 30 minutes before the feeds are started.
When addition of the feeds is completed, the reaction is continued until most (greater than about 98%) of the monomers have reacted. The reactor contents then can be cooled down and the vacuum stripped to remove unreacted monomers and to raise the solids concentration to about 42-43 percent by weight. If necessary, the pH of the latex can be adjusted to around 6.0 to about 7.0 before stripping the reaction volatiles.
EXAMPLE 2
Bioactive Anionic Latex Prepared by Late Introduction of the Bioactive Agent
An emulsion polymerization reaction can be conducted according to the details provided in Example 2, except that an approximately 32 g-sample of bioactive component can be introduced into the non-aqueous monomer feed after about 4 hours, rather than 3 hours, of the 5-hour non-aqueous monomer feed.
In the specification, typical embodiments of the invention have been disclosed and, although specific terms are employed, they are used in a generic and descriptive sense and not for purposes of limitation. This invention is further illustrated and described by the appended claims, however, it should be clearly understood that resort can be had to various other embodiments, aspects, modifications, and equivalents to those disclosed in the claims, which, after reading the description herein, may suggest themselves to one of ordinary skill in the art without departing from the spirit of the present invention or the scope of these claims. The following claims are provided to ensure that the present application meets all statutory requirements as a priority application in all jurisdictions and shall not be construed as setting forth the full scope of the present invention.